If you have enough time, MEK will eventually degrade cured epoxy, but it might take a week of immersion depending on how thick it is. Methylene Chloride will work faster, but is hard to find.
This company makes solvents for commercial semiconductor disassembly, but I suspect it is quite expensive. https://www.dynaloy.com/products